{"_buckets": {"deposit": "305f4af2-351f-4ecd-8596-5dcbb8b7470d"}, "_deposit": {"created_by": 3, "id": "6192", "owners": [3], "pid": {"revision_id": 0, "type": "depid", "value": "6192"}, "status": "published"}, "_oai": {"id": "oai:kyutech.repo.nii.ac.jp:00006192", "sets": ["20"]}, "author_link": ["18040", "25459"], "item_23_biblio_info_6": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2019-03", "bibliographicIssueDateType": "Issued"}, "bibliographicIssueNumber": "1", "bibliographicPageEnd": "012031-7", "bibliographicPageStart": "012031-1", "bibliographicVolumeNumber": "576", "bibliographic_titles": [{"bibliographic_title": "IOP Conference Series: Materials Science and Engineering"}]}]}, "item_23_description_4": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "The A1050/AZ31 clad materials were produced by vacuum roll bonding. The effects of rolling temperature and reduction rate on the interface of A1050/AZ31 clad materials were investigated, and the fracture behaviors of A1050/AZ31 interface were studied. A very thin intermetallic compound layer was formed at the A1050/AZ31 interface at rolling temperature of 350ºC and reduction rate of 25%. Therefore the A1050/AZ31 interface mainly was ductile fracture, and the average tensile strength of A1050/AZ31 interface reached the maximum (43MPa). When the rolling temperature was 450ºC and the reduction rate was 25%, the fracture occurred on the brittle intermetallic compound Al3Mg2 layer (thickness 7.68μm) and Al12Mg17 layer (thickness 1.95μm), mainly on Al3Mg2 layer, and the average tensile strength of A1050/AZ31 interface reached the minimum (0.61MPa).", "subitem_description_type": "Abstract"}]}, "item_23_description_5": {"attribute_name": "内容記述", "attribute_value_mlt": [{"subitem_description": "2019 International Conference on Advances in Materials, Mechanical and Manufacturing (AMMM 2019), 22–24 March 2019, Beijing, China", "subitem_description_type": "Other"}]}, "item_23_description_60": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"subitem_description": "Conference Paper", "subitem_description_type": "Other"}]}, "item_23_publisher_7": {"attribute_name": "出版者", "attribute_value_mlt": [{"subitem_publisher": "IOP Publishing"}]}, "item_23_relation_12": {"attribute_name": "DOI", "attribute_value_mlt": [{"subitem_relation_type": "isIdenticalTo", "subitem_relation_type_id": {"subitem_relation_type_id_text": "info:doi/10.1088/1757-899X/576/1/012031", "subitem_relation_type_select": "DOI"}}]}, "item_23_relation_14": {"attribute_name": "情報源", "attribute_value_mlt": [{"subitem_relation_type_id": {"subitem_relation_type_id_text": "https://doi.org/10.1088/1757-899X/576/1/012031", "subitem_relation_type_select": "DOI"}}]}, "item_23_rights_13": {"attribute_name": "権利", "attribute_value_mlt": [{"subitem_rights": "Creative Commons Attribution 3.0 licence."}]}, "item_23_select_59": {"attribute_name": "査読の有無", "attribute_value_mlt": [{"subitem_select_item": "yes"}]}, "item_23_source_id_8": {"attribute_name": "ISSN", "attribute_value_mlt": [{"subitem_source_identifier": "1757-899X", "subitem_source_identifier_type": "ISSN"}, {"subitem_source_identifier": "1757-8981", "subitem_source_identifier_type": "ISSN"}]}, "item_23_text_37": {"attribute_name": "著者所属", "attribute_value_mlt": [{"subitem_text_value": "Department of Materials Science, Graduate School of Engineering, Kyushu Institute of Technology, Kitakyushu 804-8550, Japan"}, {"subitem_text_value": "Department of Materials Science, Graduate School of Engineering, Kyushu Institute of Technology, Kitakyushu 804-8550, Japan"}]}, "item_23_text_62": {"attribute_name": "連携ID", "attribute_value_mlt": [{"subitem_text_value": "7898"}]}, "item_23_version_type_58": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_version_resource": "http://purl.org/coar/version/c_970fb48d4fbd8a85", "subitem_version_type": "VoR"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "Shu, J F"}], "nameIdentifiers": [{"nameIdentifier": "25459", "nameIdentifierScheme": "WEKO"}]}, {"creatorAffiliations": [{"affiliationNameIdentifiers": [], "affiliationNames": [{"affiliationName": "", "affiliationNameLang": "ja"}]}], "creatorNames": [{"creatorName": "Yamaguchi, Tomiko", "creatorNameLang": "en"}, {"creatorName": "山口, 富子", "creatorNameLang": "ja"}, {"creatorName": "ヤマグチ, トミコ", "creatorNameLang": "ja-Kana"}], "familyNames": [{"familyName": "Yamaguchi", "familyNameLang": "en"}, {"familyName": "山口", "familyNameLang": "ja"}, {"familyName": "ヤマグチ", "familyNameLang": "ja-Kana"}], "givenNames": [{"givenName": "Tomiko", "givenNameLang": "en"}, {"givenName": "富子", "givenNameLang": "ja"}, {"givenName": "トミコ", "givenNameLang": "ja-Kana"}], "nameIdentifiers": [{"nameIdentifier": "18040", "nameIdentifierScheme": "WEKO"}, {"nameIdentifier": "20243983", "nameIdentifierScheme": "e-Rad", "nameIdentifierURI": "https://nrid.nii.ac.jp/ja/nrid/1000020243983"}, {"nameIdentifier": "35328876700", "nameIdentifierScheme": "Scopus著者ID", "nameIdentifierURI": "https://www.scopus.com/authid/detail.uri?authorId=35328876700"}, {"nameIdentifier": "117", "nameIdentifierScheme": "九工大研究者情報", "nameIdentifierURI": "https://hyokadb02.jimu.kyutech.ac.jp/html/117_ja.html"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2019-09-25"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "1757-899X_576_1_012031.pdf", "filesize": [{"value": "1.3 MB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_free", "mimetype": "application/pdf", "size": 1300000.0, "url": {"label": "1757-899X_576_1_012031.pdf", "url": "https://kyutech.repo.nii.ac.jp/record/6192/files/1757-899X_576_1_012031.pdf"}, "version_id": "0c69e13f-d4f4-4012-95f2-4459ca2fbd56"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "eng"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "conference paper", "resourceuri": "http://purl.org/coar/resource_type/c_5794"}]}, "item_title": "Bond characteristics of Al/Mg clad materials produced by vacuum roll bonding", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "Bond characteristics of Al/Mg clad materials produced by vacuum roll bonding"}]}, "item_type_id": "23", "owner": "3", "path": ["20"], "permalink_uri": "http://hdl.handle.net/10228/00007402", "pubdate": {"attribute_name": "公開日", "attribute_value": "2019-09-25"}, "publish_date": "2019-09-25", "publish_status": "0", "recid": "6192", "relation": {}, "relation_version_is_last": true, "title": ["Bond characteristics of Al/Mg clad materials produced by vacuum roll bonding"], "weko_shared_id": 3}
Bond characteristics of Al/Mg clad materials produced by vacuum roll bonding
http://hdl.handle.net/10228/00007402
http://hdl.handle.net/10228/0000740296b30128-d076-446b-9858-af5a746f95df
名前 / ファイル | ライセンス | アクション |
---|---|---|
1757-899X_576_1_012031.pdf (1.3 MB)
|
|
Item type | 会議発表論文 = Conference Paper(1) | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
公開日 | 2019-09-25 | |||||||||||
資源タイプ | ||||||||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_5794 | |||||||||||
資源タイプ | conference paper | |||||||||||
タイトル | ||||||||||||
タイトル | Bond characteristics of Al/Mg clad materials produced by vacuum roll bonding | |||||||||||
言語 | ||||||||||||
言語 | eng | |||||||||||
著者 |
Shu, J F
× Shu, J F× 山口, 富子
WEKO
18040
|
|||||||||||
抄録 | ||||||||||||
内容記述タイプ | Abstract | |||||||||||
内容記述 | The A1050/AZ31 clad materials were produced by vacuum roll bonding. The effects of rolling temperature and reduction rate on the interface of A1050/AZ31 clad materials were investigated, and the fracture behaviors of A1050/AZ31 interface were studied. A very thin intermetallic compound layer was formed at the A1050/AZ31 interface at rolling temperature of 350ºC and reduction rate of 25%. Therefore the A1050/AZ31 interface mainly was ductile fracture, and the average tensile strength of A1050/AZ31 interface reached the maximum (43MPa). When the rolling temperature was 450ºC and the reduction rate was 25%, the fracture occurred on the brittle intermetallic compound Al3Mg2 layer (thickness 7.68μm) and Al12Mg17 layer (thickness 1.95μm), mainly on Al3Mg2 layer, and the average tensile strength of A1050/AZ31 interface reached the minimum (0.61MPa). | |||||||||||
備考 | ||||||||||||
内容記述タイプ | Other | |||||||||||
内容記述 | 2019 International Conference on Advances in Materials, Mechanical and Manufacturing (AMMM 2019), 22–24 March 2019, Beijing, China | |||||||||||
書誌情報 |
IOP Conference Series: Materials Science and Engineering 巻 576, 号 1, p. 012031-1-012031-7, 発行日 2019-03 |
|||||||||||
出版社 | ||||||||||||
出版社 | IOP Publishing | |||||||||||
DOI | ||||||||||||
関連タイプ | isIdenticalTo | |||||||||||
識別子タイプ | DOI | |||||||||||
関連識別子 | info:doi/10.1088/1757-899X/576/1/012031 | |||||||||||
ISSN | ||||||||||||
収録物識別子タイプ | ISSN | |||||||||||
収録物識別子 | 1757-899X | |||||||||||
ISSN | ||||||||||||
収録物識別子タイプ | ISSN | |||||||||||
収録物識別子 | 1757-8981 | |||||||||||
著作権関連情報 | ||||||||||||
権利情報 | Creative Commons Attribution 3.0 licence. | |||||||||||
出版タイプ | ||||||||||||
出版タイプ | VoR | |||||||||||
出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||||||||
査読の有無 | ||||||||||||
値 | yes | |||||||||||
連携ID | ||||||||||||
7898 | ||||||||||||
著者所属 | ||||||||||||
Department of Materials Science, Graduate School of Engineering, Kyushu Institute of Technology, Kitakyushu 804-8550, Japan | ||||||||||||
著者所属 | ||||||||||||
Department of Materials Science, Graduate School of Engineering, Kyushu Institute of Technology, Kitakyushu 804-8550, Japan | ||||||||||||
情報源 | ||||||||||||
識別子タイプ | DOI | |||||||||||
関連識別子 | https://doi.org/10.1088/1757-899X/576/1/012031 | |||||||||||
資料タイプ | ||||||||||||
内容記述タイプ | Other | |||||||||||
内容記述 | Conference Paper |