@article{oai:kyutech.repo.nii.ac.jp:00001057,
 author = {Narita, K and Yamasaki, J and Fukunaga, H},
 issue = {B11},
 journal = {Journal of Applied Physics},
 month = {Nov},
 note = {Boron content dependences of saturation magnetostriction lambda s at room temperature in as-quenched and annealed Fe100-xBx (15<or=*<or=25) and Co100-x Bx(19<or=*<or=24) amorphous alloys were measured. The value of lambda s in Fe-B alloys peaks at x=20, while lambda s in Co-B alloys decreases with increasing boron content. For two series of alloys, nearly quadratic relations between magnetostriction and saturation magnetization σ s were found. After 1 hour annealing at 250 degrees C, both lambda s and σ s in Fe-B and Co-B alloys increased. The increase in lambda s of Fe-B alloys was within 8%, and was larger than that of Co-B alloys. For annealed Fe-B and Co-B alloys, quadratic relations were also observed, which suggests that the increase in magnetostriction arises from the increase in magnetization},
 pages = {7591--7593},
 title = {Saturation magnetostriction and its annealing behavior of Fe100-xBx and Co100-xBx amorphous alloys},
 volume = {50},
 year = {1979}
}