@article{oai:kyutech.repo.nii.ac.jp:00001114,
 author = {Narita, K and Yamasaki, J and Fukunaga, H},
 issue = {5},
 journal = {IEEE Transactions on Magnetics},
 month = {Sep},
 note = {Composition dependence of the magnetic moment and Curie temperature in amorphous (FexCo100-x)100-(y+z)SiyB z ribbons has been studied systematically with changing x, y, and z. A knee suggesting a peak was found in the magnetic moment vs. metalloid content curve for Fe-Si-B alloys, while the moment of Co-Si-B alloys decreases nearly linearly with increasing metalloid content. The moment of (FeCo)-Si-B alloys decreases monotonously with decreasing iron content. A clear peak in the Curie temperature vs. metalloid content curve was found not only for Fe-Si-B alloys but also for Co-Si-B alloys. The Curie temperature of (FeCo)-Si-B alloys peaks for varying iron content independently of the amount of total metalloid contained in the alloys. These behaviors are discussed in the framework of the Slater-Bethe's curve},
 pages = {1016--1018},
 title = {Composition dependence of magnetic moment and Curie temperature in amorphous (FexCo100-x)100-(y+z)Siy Bz ribbons},
 volume = {14},
 year = {1978}
}